Plexiglas® Hi-Gloss FT15 black 9V022
Polymethyl Methacrylate Acrylic
PLEXIGLAS® Hi-Gloss FT15 black 9V022 is a special acrylic-based polymer.
With regard to its
PLEXIGLAS® Hi-Gloss FT15 9V022 shows comparable properties to those of PLEXIGLAS® standard molding compounds. In addition, PLEXIGLAS® Hi-Gloss FT15 9V022 offers the special benefit of a
Application:
PLEXIGLAS® Hi-Gloss FT15 9V022 is particularly suitable for injection molding technical components. Owing to ist superior brilliance, high-gloss (Class A) black surfaces can be obtained in.
Examples:
add-on automotive body parts
Features | - Good Flow，High Gloss，High Heat Resistance，Weather Resistant
|
Uses | - Automotive Applications，Automotive Exterior Parts
|
Appearance | |
Forms | |
Processing Method | |
Density | 1.19 | g/cm³ | ISO 1183 |
Melt Volume-Flow Rate (MVR) (230°C/3.8 kg) | 0.275 | in³/10min | ISO 1133 |
Tensile Modulus | 508000 | psi | ISO 527-2/1 |
Tensile Stress (Break) | 7250 | psi | ISO 527-2/5 |
Tensile Strain (Break) | 3.1 | % | ISO 527-2/5 |
Charpy Unnotched Impact Strength (73°F) | 8.6 | ft·lb/in² | ISO 179/1eU |
Heat Deflection Temperature |
|
|
|
66 psi, Unannealed | 225 | °F | ISO 75-2/B |
264 psi, Unannealed | 221 | °F | ISO 75-2/A |
Glass Transition Temperature | 250 | °F | ISO 11357-2 |
Vicat Softening Temperature | 239 | °F | ISO 306/B50 |
Glow Wire Ignition Temperature | 1250 | °F | IEC 60695-2-13 |
Drying Temperature | 212 | °F |
|
Drying Time | 4.0 to 6.0 | hr |
|
Processing (Melt) Temp | 428 to 482 | °F |
|
Mold Temperature | 158 to 203 | °F |
|