Radilon® A ERV1906LK 100 NAT
Polyamide 66
PA66 13% glass fiber reinforced injection moulding grade. Toughened, lubricated and heat stabilized. Natural colour.
Suitable for parts requiring improved impact strength along with enhanced stiffness.
A typical application are anti-vibration rings.
Filler / Reinforcement | |
Additive | - Heat Stabilizer，Lubricant
|
Features | - Good Impact Resistance，Good Stiffness，Heat Stabilized，Lubricated
|
RoHS Compliance | |
Appearance | |
Processing Method | |
Resin ID (ISO 1043) | |
Density | 1.22 | -- | g/cm³ | ISO 1183 |
Molding Shrinkage 2 |
|
|
| ISO 294-4 |
Across Flow | 0.80 | -- | % |
|
Flow | 0.40 | -- | % |
|
Water Absorption |
|
|
| ISO 62 |
Saturation, 73°F, 0.0787 in | 7.5 | -- | % |
|
Equilibrium, 73°F, 0.0787 in, 50% RH | 1.9 | -- | % |
|
Tensile Modulus | 725000 | 609000 | psi | ISO 527-2/1A/1 |
Tensile Stress |
|
|
|
|
Yield | -- | 10900 | psi | ISO 527-2/1A/50 |
Break | 14500 | -- | psi | ISO 527-2/1A/5 |
Tensile Strain |
|
|
|
|
Yield | -- | 8.0 | % | ISO 527-2/1A/50 |
Break | 4.0 | -- | % | ISO 527-2/1A/5 |
Nominal Tensile Strain at Break | -- | 17 | % | ISO 527-2/1A/50 |
Flexural Modulus 3 | 624000 | -- | psi | ISO 178 |
Flexural Stress 3 | 21800 | -- | psi | ISO 178 |
Charpy Notched Impact Strength |
|
|
| ISO 179/1eA |
-22°F | 2.3 | 2.4 | ft·lb/in² |
|
73°F | 5.5 | 7.1 | ft·lb/in² |
|
Charpy Unnotched Impact Strength |
|
|
| ISO 179/1eU |
-22°F | 19 | 20 | ft·lb/in² |
|
73°F | 36 | 48 | ft·lb/in² |
|
Heat Deflection Temperature |
|
|
|
|
66 psi, Unannealed | 446 | -- | °F | ISO 75-2/Bf |
264 psi, Unannealed | 347 | -- | °F | ISO 75-2/Af |
Vicat Softening Temperature | 455 | -- | °F | ISO 306/B50 |
Melting Temperature 4 | 500 | -- | °F | ISO 11357-3 |
Surface Resistivity 5 | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
Volume Resistivity 5 | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
Comparative Tracking Index(Solution A) | 550 | -- | V | IEC 60112 |
Flame Rating (0.031 in) | HB | -- |
| UL 94 |
Glow Wire Flammability Index (0.08 in) | 1290 | -- | °F | IEC 60695-2-12 |
Flammability | < 10.0 | -- | mm/min | FMVSS 302 |
Drying Temperature - Desiccant Dryer | 176 | °F |
|
Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr |
|
Dew Point - Desiccant Dryer | -4 | °F |
|
Suggested Max Moisture | 0.15 | % |
|
Processing (Melt) Temp | 536 to 572 | °F |
|
Mold Temperature | 176 to 212 | °F |
|
Injection Rate | Moderate-Fast |
|
|