Radilon® A USX016W 100 NAT
Polyamide 66
PA66 injection moulding grade. Toughened, heat stabilized. Natural colour.
Suitable for parts requiring excellent impact resistance and high flexibility.
Very good properties retention after ageing.
Additive | |
Features | - Good Impact Resistance，Heat Aging Resistant，Heat Stabilized，High Flexibility
|
RoHS Compliance | |
Appearance | |
Processing Method | |
Resin ID (ISO 1043) | |
Density | 1.08 | -- | g/cm³ | ISO 1183 |
Water Absorption |
|
|
| ISO 62 |
Saturation, 73°F, 0.0787 in | 6.3 | -- | % |
|
Equilibrium, 73°F, 0.0787 in, 50% RH | 1.8 | -- | % |
|
Tensile Modulus | 283000 | 138000 | psi | ISO 527-2/1A/1 |
Tensile Stress (Yield) | 7250 | 5800 | psi | ISO 527-2/1A/50 |
Tensile Strain (Yield) | 12 | 30 | % | ISO 527-2/1A/50 |
Nominal Tensile Strain at Break | 45 | > 50 | % | ISO 527-2/1A/50 |
Flexural Modulus 2 | 268000 | 116000 | psi | ISO 178 |
Flexural Stress 2 | 10200 | 58000 | psi | ISO 178 |
Charpy Notched Impact Strength(73°F) | 26 | 38 | ft·lb/in² | ISO 179/1eA |
Heat Deflection Temperature |
|
|
|
|
66 psi, Unannealed | 302 | -- | °F | ISO 75-2/Bf |
264 psi, Unannealed | 158 | -- | °F | ISO 75-2/Af |
Vicat Softening Temperature | 392 | -- | °F | ISO 306/B50 |
Melting Temperature 3 | 500 | -- | °F | ISO 11357-3 |
Surface Resistivity 4 | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
Volume Resistivity 4 | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
Comparative Tracking Index(Solution A) | 600 | -- | V | IEC 60112 |
Flame Rating (0.031 in) | HB | -- |
| UL 94 |
Glow Wire Flammability Index (0.08 in) | 1200 | -- | °F | IEC 60695-2-12 |
Flammability | < 1 | -- | in/min | FMVSS 302 |
Drying Temperature - Desiccant Dryer | 176 | °F |
|
Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr |
|
Dew Point - Desiccant Dryer | -4 | °F |
|
Suggested Max Moisture | 0.15 | % |
|
Processing (Melt) Temp | 518 to 554 | °F |
|
Mold Temperature | 140 to 176 | °F |
|
Injection Rate | Moderate |
|
|