VICTREX HT™ POLYMER 22GL30
High performance thermoplastic material, 30% glass fibre reinforced PolyEtherKetone (PEK), semi crystalline, granules for injection moulding, standard flow, colour natural/beige.
Higher temperature applications where higher strength in a static system is required. Low coefficient of thermal expansion. Chemically resistant to aggressive environments, suitable for sterilisation for medical and food contact applications。
Material Properties |
Physical | Nominal Value | Unit | Test Method |
Density (Crystalline) | 1.53 | g/cm³ | ISO 1183 |
Spiral Flow 1 | 10.5 | cm | Internal Method |
Molding Shrinkage 2 |
|
| ISO 294-4 |
Across Flow | 0.90 | % |
|
Flow | 0.30 | % |
|
Water Absorption (Saturation, 23°C) | 0.50 | % | ISO 62 |
Water Absorption Saturation (100°C) | 0.60 | % | ISO 62 |
Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus (23°C) | 12000 | MPa | ISO 527-1 |
Tensile Stress |
|
| ISO 527-2 |
Break, 23°C | 195 | MPa |
|
Break, 125°C | 125 | MPa |
|
Break, 175°C | 75.0 | MPa |
|
Break, 225°C | 65.0 | MPa |
|
Break, 275°C | 55.0 | MPa |
|
Tensile Strain (Break, 23°C) | 2.6 | % | ISO 527-2 |
Flexural Modulus (23°C) | 11000 | MPa | ISO 178 |
Flexural Stress |
|
| ISO 178 |
23°C | 290 | MPa |
|
125°C | 210 | MPa |
|
175°C | 120 | MPa |
|
275°C | 85.0 | MPa |
|
Compressive Stress |
|
| ISO 604 |
23°C | 290 | MPa |
|
120°C | 180 | MPa |
|
200°C | 75.0 | MPa |
|
250°C | 50.0 | MPa |
|
Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | ISO 179/1eA |
Charpy Unnotched Impact Strength (23°C) | 70.0 | kJ/m² | ISO 179/1U |
Notched Izod Impact Strength (23°C) | 8.8 | kJ/m² | ISO 180/A |
Unnotched Izod Impact Strength (23°C) | 70.0 | kJ/m² | ISO 180 |
Hardness | Nominal Value | Unit | Test Method |
Shore Hardness (Shore D, 23°C) | 87.5 |
| ISO 868 |
Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load (1.8 MPa, Unannealed) | 360 | °C | ISO 75-2/Af |
Glass Transition Temperature |
|
| ISO 11357-2 |
Onset | 152 | °C |
|
Midpoint | 160 | °C |
|
Melting Temperature | 373 | °C | ISO 11357-3 |
CLTE - Flow |
|
| ISO 11359-2 |
< 152°C | 20 | ppm/K |
|
> 152°C | 25 | ppm/K |
|
CLTE - Average |
|
| ISO 11359-2 |
< 152°C | 45 | ppm/K |
|
> 152°C | 110 | ppm/K |
|
Thermal Conductivity |
|
| ISO 22007-4 |
23°C 3 | 0.30 | W/m/K |
|
23°C 4 | 0.35 | W/m/K |
|
Electrical | Nominal Value | Unit | Test Method |
Volume Resistivity (23°C) | 1.0E+16 | ohms·cm | IEC 60093 |
Dielectric Strength (2.00 mm) | 23.0 | kV/mm | IEC 60243-1 |
Dielectric Constant (23°C, 1 kHz) | 3.20 |
| IEC 60250 |
Dissipation Factor (23°C, 1 MHz) | 5.0E-3 |
| IEC 60250 |
Comparative Tracking Index | 150 | V | IEC 60112 |
Flammability | Nominal Value | Unit | Test Method |
Glow Wire Flammability Index (2.0 mm) | 960 | °C | IEC 60695-2-12 |
Fill Analysis | Nominal Value | Unit | Test Method |
Melt Viscosity (400°C) | 450 | Pa·s | ISO 11443 |