Products

CYCOLOY™ Resin C1200HF

CYCOLOY™ Resin C1200HF

Manufacturer: SABIC
Produced At: Import/ China
Product Category: Polycarbonate + ABS
Product No: CYCOLOY Resin C1200HF
Product Quantity: 25KG / BAG
Product Features: Ductile，Good Flow，Good Impact Resistance，High Heat Resistance

CYCOLOY™ Resin C1200HF

Polycarbonate + ABS
Product Description:
PC+ABS, excellent flow/impact/high heat resistance. Low temperature ductility.
Features 
DuctileGood FlowGood Impact ResistanceHigh Heat Resistance 
Processing Method 

  • Injection Molding

Multi-Point Data 

  • Coefficient of Thermal Expansion vs. Temperature (ASTM E831)

  • Elastic Modulus vs Temperature (ASTM D4065)

  • Flexural DMA (ASTM D4065)

  • Instrumented Impact (Energy) (ASTM D3763)

  • Instrumented Impact (Load) (ASTM D3763)

  • Pressure-Volume-Temperature (PVT - Zoller Method)

  • Shear DMA (ASTM D4065)

  • Specific Heat vs. Temperature (ASTM D3417)

  • Tensile Creep (ASTM D2990)

  • Tensile Fatigue

  • Tensile Stress vs. Strain (ASTM D638)

  • Thermal Conductivity vs. Temperature (ASTM E1530)

  • Viscosity vs. Shear Rate (ASTM D3835)

Physical
Nominal Value
Unit
Test Method
Density / Specific Gravity
1.15

ASTM D792
Melt Mass-Flow Rate (MFR) (260°C/5.0 kg)
19
g/10 min
ASTM D1238
Melt Volume-Flow Rate (MVR) (265°C/5.0 kg)
1.46
in³/10min
ISO 1133
Molding Shrinkage - Flow (0.126 in)
5.0E-3 to 7.0E-3
in/in
Internal Method
Mechanical
Nominal Value
Unit
Test Method
Tensile Modulus



-- 3
330000
psi
ASTM D638
--
344000
psi
ISO 527-2/1
Tensile Strength



Yield 4
8300
psi
ASTM D638
Yield
7980
psi
ISO 527-2/50
Tensile Elongation



Yield 4
5.0
%
ASTM D638
Yield
4.8
%
ISO 527-2/50
Break 4
150
%
ASTM D638
Break
110
%
ISO 527-2/50
Flexural Modulus



1.97 in Span 5
340000
psi
ASTM D790
--
327000
psi
ISO 178
Flexural Stress



--
12500
psi
ISO 178
Yield, 1.97 in Span 5
12800
psi
ASTM D790
Impact
Nominal Value
Unit
Test Method
Notched Izod Impact



-22°F
9.0
ft·lb/in
ASTM D256
73°F
11
ft·lb/in
ASTM D256
-22°F 6
16
ft·lb/in²
ISO 180/1A
73°F 6
23
ft·lb/in²
ISO 180/1A
Instrumented Dart Impact


ASTM D3763
-22°F, Total Energy
480
in·lb

73°F, Total Energy
480
in·lb

Thermal
Nominal Value
Unit
Test Method
Deflection Temperature Under Load



66 psi, Unannealed, 0.126 in
265
°F
ASTM D648
66 psi, Unannealed, 2.52 in Span 7
266
°F
ISO 75-2/Bf
264 psi, Unannealed, 0.126 in
235
°F
ASTM D648
264 psi, Unannealed, 2.52 in Span 7
230
°F
ISO 75-2/Af
Vicat Softening Temperature
266
°F
ISO 306/B50
CLTE - Flow (-40 to 104°F)
4.0E-5
in/in/°F
ASTM E831
RTI Elec
221
°F
UL 746
RTI Imp
176
°F
UL 746
RTI Str
221
°F
UL 746
Electrical
Nominal Value

Test Method
Comparative Tracking Index (CTI)
PLC 2

UL 746
High Amp Arc Ignition (HAI)
PLC 1

UL 746
Hot-wire Ignition (HWI)
PLC 3

UL 746
Flammability
Nominal Value

Test Method
Flame Rating (0.05 in)
HB

UL 94
Injection
Nominal Value
Unit

Drying Temperature
212 to 230
°F

Drying Time
3.0 to 4.0
hr

Drying Time, Maximum
8.0
hr

Suggested Max Moisture
0.020
%

Suggested Shot Size
30 to 80
%

Hopper Temperature
140 to 176
°F

Rear Temperature
482 to 554
°F

Middle Temperature
491 to 563
°F

Front Temperature
500 to 572
°F

Nozzle Temperature
527 to 572
°F

Processing (Melt) Temp
527 to 572
°F

Mold Temperature
140 to 194
°F

Back Pressure
43.5 to 102
psi

Screw Speed
40 to 70
rpm

Vent Depth
1.5E-3 to 3.0E-3
in


Products are widely used in plastic modification, automotive, construction, electrical and electronic, industrial, daily necessities and other fields