VICTREX™ PEEK POLYMER 650G
High performance thermoplastic material, unreinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding and extrusion, low flow, colour natural/beige.
Applications for higher strength and stiffness as well as enhanced ductility. Chemically resistant to aggressive environments, suitable for sterilisation for medical and food contact applications.
Material Properties |
Physical | Nominal Value | Unit | Test Method |
Density (Crystalline) | 1.30 | g/cm³ | ISO 1183 |
Spiral Flow |
|
| Internal Method |
-- 1 | 12.5 | cm |
|
-- 2 | 63.0 | cm |
|
-- 3 | 70.0 | cm |
|
Molding Shrinkage 4 |
|
| ISO 294-4 |
Across Flow | 1.3 | % |
|
Flow | 0.90 | % |
|
Water Absorption (Saturation, 23°C) | 0.45 | % | ISO 62 |
Water Absorption Saturation (100°C) | 0.55 | % | ISO 62 |
Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus (23°C) | 3900 | MPa | ISO 527-1 |
Tensile Stress (Yield, 23°C) | 95.0 | MPa | ISO 527-2 |
Tensile Strain (Break, 23°C) | 32 | % | ISO 527-2 |
Flexural Modulus (23°C) | 3600 | MPa | ISO 178 |
Flexural Stress |
|
| ISO 178 |
3.5% Strain, 23°C | 120 | MPa |
|
23°C 5 | 155 | MPa |
|
125°C | 85.0 | MPa |
|
175°C | 16.0 | MPa |
|
275°C | 9.00 | MPa |
|
Compressive Stress |
|
| ISO 604 |
23°C | 120 | MPa |
|
120°C | 65.0 | MPa |
|
Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength (23°C) | 10.0 | kJ/m² | ISO 179/eA |
Charpy Unnotched Impact Strength (23°C) | No Break |
| ISO 179 |
Notched Izod Impact Strength (23°C) | 7.2 | kJ/m² | ISO 180/A |
Unnotched Izod Impact Strength (23°C) | No Break |
| ISO 180 |
Hardness | Nominal Value | Unit | Test Method |
Shore Hardness (Shore D, 23°C) | 84.0 |
| ISO 868 |
Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load |
|
| ISO 75-2/Af |
1.8 MPa, Unannealed | 152 | °C |
|
1.8 MPa, Annealed 6 | 168 | °C |
|
Glass Transition Temperature |
|
| ISO 11357-2 |
Onset | 143 | °C |
|
Midpoint | 150 | °C |
|
Melting Temperature | 343 | °C | ISO 11357-3 |
CLTE - Flow |
|
| ISO 11359-2 |
< 143°C | 45 | ppm/K |
|
> 143°C | 125 | ppm/K |
|
CLTE - Average |
|
| ISO 11359-2 |
< 143°C | 65 | ppm/K |
|
> 143°C | 160 | ppm/K |
|
Thermal Conductivity |
|
| ISO 22007-4 |
23°C 7 | 0.29 | W/m/K |
|
23°C 8 | 0.32 | W/m/K |
|
Electrical | Nominal Value | Unit | Test Method |
Volume Resistivity |
|
| IEC 60093 |
23°C | 1.0E+16 | ohms·cm |
|
125°C | 1.0E+15 | ohms·cm |
|
275°C | 1.0E+9 | ohms·cm |
|
Dielectric Strength (2.00 mm) | 23.0 | kV/mm | IEC 60243-1 |
Dielectric Constant (23°C, 1 kHz) | 3.10 |
| IEC 60250 |
Dissipation Factor (23°C, 1 MHz) | 5.0E-3 |
| IEC 60250 |
Comparative Tracking Index | 150 | V | IEC 60112 |
Flammability | Nominal Value | Unit | Test Method |
Glow Wire Flammability Index (2.0 mm) | 960 | °C | IEC 60695-2-12 |
Fill Analysis | Nominal Value | Unit | Test Method |
Melt Viscosity (400°C) | 475 | Pa·s | ISO 11443 |