CYCOLOY™ FR Resin CY6110
聚碳酸酯+丙烯腈丁二烯苯乙烯
产品说明:
CYCOLOY CY6110 Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) resin is a hydrolytically stable, impact modified grade that can be injection molded. This non-chlorinated, non-brominated flame retardant PC/ABS has a UL V0 & 5VB flame rating. CYCOLOY CY6110 resin is an excellent candidate for a wide variety of large size of applications including appliances, lighting, electrical and enclosures.
添加剂 | |
特性 | - Chlorine Free、抗撞击性，良好、良好的流动性、水解稳定、无溴、阻燃性
|
用途 | - Lighting Applications、电气/电子应用领域、电器用具、电子显示器
|
加工方法 | |
Also Available In | |
密度 | 1.18 | g/cm³ | ISO 1183 |
熔融体积流量（MVR） (260°C/2.16 kg) | 1.40 | in³/10min | ISO 1133 |
收缩率 - 流动 (0.126 in) | 4.0E-3 到 6.0E-3 | in/in | 内部方法 |
吸水率 |
|
| ISO 62 |
饱和, 73°F | 0.60 | % |
|
平衡, 73°F, 50% RH | 0.20 | % |
|
拉伸模量 |
|
|
|
-- 3 | 400000 | psi | ASTM D638 |
-- | 399000 | psi | ISO 527-2/1 |
抗张强度 |
|
|
|
屈服 4 | 9140 | psi | ASTM D638 |
屈服 | 9140 | psi | ISO 527-2/50 |
断裂 4 | 6820 | psi | ASTM D638 |
断裂 | 6670 | psi | ISO 527-2/50 |
伸长率 |
|
|
|
屈服 4 | 4.1 | % | ASTM D638 |
屈服 | 4.0 | % | ISO 527-2/50 |
断裂 4 | 65 | % | ASTM D638 |
断裂 | 35 | % | ISO 527-2/50 |
弯曲模量 5 | 354000 | psi | ISO 178 |
弯曲应力 5, 6 | 13600 | psi | ISO 178 |
简支梁缺口冲击强度 |
|
| ISO 179/1eA |
-22°F 7 | 4.8 | ft·lb/in² |
|
73°F 7 | 21 | ft·lb/in² |
|
73°F 8 | 16 | ft·lb/in² |
|
悬壁梁缺口冲击强度 |
|
|
|
-22°F | 1.9 | ft·lb/in | ASTM D256 |
73°F | 8.9 | ft·lb/in | ASTM D256 |
-22°F 9 | 4.8 | ft·lb/in² | ISO 180/1A |
-22°F 10 | 5.7 | ft·lb/in² | ISO 180/1A |
73°F 9 | 21 | ft·lb/in² | ISO 180/1A |
73°F 10 | 12 | ft·lb/in² | ISO 180/1A |
热变形温度 10 |
|
|
|
66 psi, 未退火, 0.157 in, 2.52 in 跨距 | 208 | °F | ISO 75-2/Bf |
264 psi, 未退火, 0.157 in, 2.52 in 跨距 | 190 | °F | ISO 75-2/Af |
维卡软化温度 |
|
|
|
-- | 219 | °F | ISO 306/B50 |
-- | 223 | °F | ISO 306/B120 |
Ball Pressure Test (163 到 171°F) | 通过 |
| IEC 60695-10-2 |
线形热膨胀系数 |
|
| ISO 11359-2 |
流动 : -40 到 104°F | 4.4 | in/in/°F |
|
横向 : -40°F | 4.4 | in/in/°F |
|
RTI Elec | 185 | °F | UL 746 |
RTI Imp | 185 | °F | UL 746 |
RTI | 185 | °F | UL 746 |
表面电阻率 | 1.0E+15 | ohms | IEC 60093 |
体积电阻率 | 1.0E+15 | ohms·cm | IEC 60093 |
介电强度 |
|
| IEC 60243-1 |
0.0315 in, 在油中 | 1200 | V/mil |
|
0.0630 in, 在油中 | 790 | V/mil |
|
相对电容率 |
|
| IEC 60250 |
50 Hz | 2.90 |
|
|
60 Hz | 2.90 |
|
|
1 MHz | 2.90 |
|
|
耗散因数 |
|
| IEC 60250 |
50 Hz | 2.0E-3 |
|
|
60 Hz | 2.0E-3 |
|
|
1 MHz | 7.0E-3 |
|
|
相比耐漏电起痕指数(CTI) | PLC 2 |
| UL 746 |
热丝引燃 (HWI) | PLC 3 |
| UL 746 |
UL 阻燃等级 |
|
| UL 94 |
0.06 in | V-0 |
|
|
0.10 in | 5VB |
|
|
灼热丝易燃指数 (0.04 in) | 1760 | °F | IEC 60695-2-12 |
热灯丝点火温度 |
|
| IEC 60695-2-13 |
0.04 in | 1520 | °F |
|
0.08 in | 1520 | °F |
|
0.12 in | 1520 | °F |
|
极限氧指数 | 31 | % | ISO 4589-2 |
干燥温度 | 176 到 194 | °F |
|
干燥时间 | 2.0 到 4.0 | hr |
|
建议的最大水分含量 | 0.020 | % |
|
料斗温度 | 140 到 176 | °F |
|
料筒后部温度 | 446 到 536 | °F |
|
料筒中部温度 | 464 到 554 | °F |
|
料筒前部温度 | 482 到 572 | °F |
|
射嘴温度 | 482 到 572 | °F |
|
加工（熔体）温度 | 482 到 572 | °F |
|
模具温度 | 140 到 185 | °F |
|
排气孔深度 | 1.2E-3 到 3.0E-3 | in |
|