CYCOLOY™ FR Resin XCM840
聚碳酸酯+丙烯腈丁二烯苯乙烯
产品说明:
High stiffness PC/ABS blend offering practical impact, low CTE, high heat resistance, with good aesthetics suitable for injection molding
密度 / 比重 |
|
|
|
-- | 1.27 |
| ASTM D792 |
-- | 1.27 | g/cm³ | ISO 1183 |
熔融体积流量（MVR） |
|
| ISO 1133 |
260°C/5.0 kg | 0.610 | in³/10min |
|
265°C/5.0 kg | 0.732 | in³/10min |
|
收缩率 |
|
| 内部方法 |
流动 : 0.126 in | 5.0E-3 到 7.0E-3 | in/in |
|
横向流动 : 0.126 in | 5.0E-3 到 7.0E-3 | in/in |
|
拉伸模量 |
|
|
|
-- 2 | 624000 | psi | ASTM D638 |
-- | 624000 | psi | ISO 527-2/1 |
抗张强度 |
|
|
|
屈服 3 | 8120 | psi | ASTM D638 |
屈服 | 8120 | psi | ISO 527-2/5 |
断裂 3 | 6820 | psi | ASTM D638 |
断裂 | 6820 | psi | ISO 527-2/5 |
伸长率 |
|
|
|
屈服 3 | 4.0 | % | ASTM D638 |
屈服 | 4.0 | % | ISO 527-2/5 |
断裂 | 50 | % | ISO 527-2/5 |
弯曲模量 4 | 580000 | psi | ISO 178 |
弯曲应力 4, 5 | 14500 | psi | ISO 178 |
简支梁缺口冲击强度 6 |
|
| ISO 179/1eA |
-22°F | 4.8 | ft·lb/in² |
|
73°F | 18 | ft·lb/in² |
|
悬壁梁缺口冲击强度 7 |
|
| ISO 180/1A |
-22°F | 3.8 | ft·lb/in² |
|
73°F | 7.1 | ft·lb/in² |
|
装有测量仪表的落镖冲击 (73°F, Total Energy) | 531 | in·lb | ASTM D3763 |
载荷下热变形温度 |
|
|
|
264 psi, 未退火, 0.126 in | 248 | °F | ASTM D648 |
264 psi, 未退火, 0.157 in, 2.52 in 跨距 8 | 248 | °F | ISO 75-2/Af |
维卡软化温度 | 280 | °F | ISO 306/B50 |
线形热膨胀系数 |
|
|
|
流动 : -40 到 104°F | 2.6E-5 | in/in/°F | ASTM E831, ISO 11359-2 |
横向 : -40 到 104°F | 3.4E-5 | in/in/°F | ASTM E831 |
横向 : -40°F | 3.4E-5 | in/in/°F | ISO 11359-2 |
干燥温度 | 248 到 257 | °F |
|
干燥时间 | 4.0 到 6.0 | hr |
|
建议的最大水分含量 | 0.010 | % |
|
建议注射量 | 30 到 80 | % |
|
料筒后部温度 | 500 到 518 | °F |
|
料筒中部温度 | 509 到 554 | °F |
|
料筒前部温度 | 518 到 572 | °F |
|
射嘴温度 | 500 到 554 | °F |
|
加工（熔体）温度 | 518 到 572 | °F |
|
模具温度 | 140 到 212 | °F |
|
背压 | 43.5 到 102 | psi |
|
螺杆转速 | 40 到 70 | rpm |
|
排气孔深度 | 1.5E-3 到 3.0E-3 | in |
|