CYCOLOY™ Resin C1200HF
聚碳酸酯+丙烯腈丁二烯苯乙烯
产品说明:
PC+ABS, excellent flow/impact/high heat resistance. Low temperature ductility.
特性 | |
加工方法 | |
多点数据 | Coefficient of Thermal Expansion vs. Temperature (ASTM E831) Elastic Modulus vs Temperature (ASTM D4065) Flexural DMA (ASTM D4065) Instrumented Impact (Energy) (ASTM D3763) Instrumented Impact (Load) (ASTM D3763) Pressure-Volume-Temperature (PVT - Zoller Method) Shear DMA (ASTM D4065) Specific Heat vs. Temperature (ASTM D3417) Tensile Creep (ASTM D2990) Tensile Fatigue Tensile Stress vs. Strain (ASTM D638) Thermal Conductivity vs. Temperature (ASTM E1530) Viscosity vs. Shear Rate (ASTM D3835)
|
密度 / 比重 | 1.15 |
| ASTM D792 |
熔流率（熔体流动速率） (260°C/5.0 kg) | 19 | g/10 min | ASTM D1238 |
熔融体积流量（MVR） (265°C/5.0 kg) | 1.46 | in³/10min | ISO 1133 |
收缩率 - 流动 (0.126 in) | 5.0E-3 到 7.0E-3 | in/in | 内部方法 |
拉伸模量 |
|
|
|
-- 3 | 330000 | psi | ASTM D638 |
-- | 344000 | psi | ISO 527-2/1 |
抗张强度 |
|
|
|
屈服 4 | 8300 | psi | ASTM D638 |
屈服 | 7980 | psi | ISO 527-2/50 |
伸长率 |
|
|
|
屈服 4 | 5.0 | % | ASTM D638 |
屈服 | 4.8 | % | ISO 527-2/50 |
断裂 4 | 150 | % | ASTM D638 |
断裂 | 110 | % | ISO 527-2/50 |
弯曲模量 |
|
|
|
1.97 in 跨距 5 | 340000 | psi | ASTM D790 |
-- | 327000 | psi | ISO 178 |
弯曲应力 |
|
|
|
-- | 12500 | psi | ISO 178 |
屈服, 1.97 in 跨距 5 | 12800 | psi | ASTM D790 |
悬壁梁缺口冲击强度 |
|
|
|
-22°F | 9.0 | ft·lb/in | ASTM D256 |
73°F | 11 | ft·lb/in | ASTM D256 |
-22°F 6 | 16 | ft·lb/in² | ISO 180/1A |
73°F 6 | 23 | ft·lb/in² | ISO 180/1A |
装有测量仪表的落镖冲击 |
|
| ASTM D3763 |
-22°F, Total Energy | 480 | in·lb |
|
73°F, Total Energy | 480 | in·lb |
|
载荷下热变形温度 |
|
|
|
66 psi, 未退火, 0.126 in | 265 | °F | ASTM D648 |
66 psi, 未退火, 2.52 in 跨距 7 | 266 | °F | ISO 75-2/Bf |
264 psi, 未退火, 0.126 in | 235 | °F | ASTM D648 |
264 psi, 未退火, 2.52 in 跨距 7 | 230 | °F | ISO 75-2/Af |
维卡软化温度 | 266 | °F | ISO 306/B50 |
线形热膨胀系数 - 流动 (-40 到 104°F) | 4.0E-5 | in/in/°F | ASTM E831 |
RTI Elec | 221 | °F | UL 746 |
RTI Imp | 176 | °F | UL 746 |
RTI | 221 | °F | UL 746 |
相比耐漏电起痕指数(CTI) | PLC 2 |
| UL 746 |
高电弧燃烧指数(HAI) | PLC 1 |
| UL 746 |
热丝引燃 (HWI) | PLC 3 |
| UL 746 |
UL 阻燃等级 (0.05 in) | HB |
| UL 94 |
干燥温度 | 212 到 230 | °F |
|
干燥时间 | 3.0 到 4.0 | hr |
|
干燥时间，最大 | 8.0 | hr |
|
建议的最大水分含量 | 0.020 | % |
|
建议注射量 | 30 到 80 | % |
|
料斗温度 | 140 到 176 | °F |
|
料筒后部温度 | 482 到 554 | °F |
|
料筒中部温度 | 491 到 563 | °F |
|
料筒前部温度 | 500 到 572 | °F |
|
射嘴温度 | 527 到 572 | °F |
|
加工（熔体）温度 | 527 到 572 | °F |
|
模具温度 | 140 到 194 | °F |
|
背压 | 43.5 到 102 | psi |
|
螺杆转速 | 40 到 70 | rpm |
|
排气孔深度 | 1.5E-3 到 3.0E-3 | in |
|
如需沙伯基础（SABIC）原厂物性表及相关文件，请联系我们工作人员，谢谢！