Akulon® FC-X9201
聚酰胺6
产品说明:
Very High Viscosity, Lubricated, Nucleated, Film Extrusion
Special Features:
Used In:
Akulon® is our family of high performance polyamide 6 and polyamide 66 materials, used by customers across the world in applications ranging from automotive, electronics & electrical, to furniture and packaging.
We offer Akulon® grades for injection molding, blow molding and extrusion (including barrier film, stock shapes, convoluted tubes, and mono and multi filament).
In molded parts the material offers an excellent balance of easy design and processing with outstanding mechanical properties over a wide temperature range and in diverse conditions. Meanwhile for extrusion the strength, resilience and easy processing of Akulon® sets the market standards.
添加剂 | |
特性 | |
用途 | |
加工方法 | |
树脂ID (ISO 1043) | |
密度 | 1.13 | g/cm³ | ISO 1183 |
吸水率 |
|
| ISO 62 |
饱和, 73°F | 9.0 | % |
|
平衡, 73°F, 50% RH | 2.5 | % |
|
粘数 | 245 | cm³/g | ISO 307 |
摩擦系数 |
|
| ISO 8295 |
Dynamic | 0.80 |
|
|
Static | 1.4 |
|
|
拉伸模量 2 | 67400 | psi | 内部方法 |
拉伸应力 - MD |
|
| ISO 527-3 |
屈服 | 4930 | psi |
|
断裂 | 13600 | psi |
|
伸长率 - MD (断裂) | 350 | % | ISO 527-3 |
Trouser Tear - Parallel | 32.0 |
| ISO 6383-1 |
水气透过率 (73°F, 85% RH) | 2.3 | g/100 in²/24 hr | DIS 15106-1/-3 |
氧气传输速率 |
|
| DIS 15105-1/-2 |
0% RH : 73°F | 23 | cm³/m²/bar/24 hr |
|
85% RH : 73°F | 33 | cm³/m²/bar/24 hr |
|
熔融温度 3 | 428 | °F | ISO 11357-3 |
线形热膨胀系数 - 流动 | 5.0E-5 | in/in/°F | ISO 11359-2 |
Specific Heat Capacity | 0.370 | Btu/lb/°F |
|
熔体粘度 (500°F) | 2.25E+6 | mPa·s | 内部方法 |
Average Specific Heat Capacity (68 到 302°F) | 0.538 | Btu/lb/°F |
|
Puncture Resistance | 24.9 | ft·lb/in | 内部方法 |
RSV - Formic Acid, 1g/100ml | 3.60 |
| 内部方法 |
干燥温度 | 176 | °F |
|
干燥时间 | 4.0 到 8.0 | hr |
|
料筒后部温度 | 446 到 455 | °F |
|
料筒中部温度 | 455 到 482 | °F |
|
料筒前部温度 | 464 到 500 | °F |
|
射嘴温度 | 464 到 518 | °F |
|
加工（熔体）温度 | 464 到 527 | °F |
|
模具温度 | 122 到 176 | °F |
|
注射速度 | 中等偏快 |
|
|
背压 | 435 到 1450 | psi |
|
螺杆压缩比 | 2.5:1.0 |
|
|