Ultramid® B3EG6
聚酰胺6
产品说明:
Ultramid B3EG6 is a 30% glass fiber reinforced injection molding PA6 grade.
Applications
Typical applications include industrial articles and electrical insulating parts.
填料/增强材料 | 玻璃纤维增强材料, 30% 填料按重量 |
特性 | 耐油性能 |
用途 | 电子绝缘、工业应用 |
机构评级 | EC 1907/2006 (REACH) |
RoHS 合规性 | RoHS 合规 |
形式 | 粒子 |
加工方法 | 注射成型 |
多点数据 | Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2) |
密度 / 比重 |
|
|
|
|
-- | 1.36 | -- |
| ASTM D792 |
-- | 1.36 | -- | g/cm³ | ISO 1183 |
熔融体积流量（MVR） (275°C/5.0 kg) | 3.05 | -- | in³/10min | ISO 1133 |
收缩率 - 流动 (0.125 in) | 3.0E-3 | -- | in/in |
|
吸水率 |
|
|
|
|
饱和 | 6.6 | -- | % | ASTM D570 |
饱和, 73°F | 6.6 | -- | % | ISO 62 |
平衡, 50% RH | 2.1 | -- | % | ASTM D570 |
平衡, 73°F, 50% RH | 2.1 | -- | % | ISO 62 |
拉伸模量 (73°F) | 1.38E+6 | 899000 | psi | ISO 527-2 |
抗张强度 |
|
|
|
|
断裂, 73°F | 24900 | -- | psi | ASTM D638 |
断裂, 73°F | 26800 | 16700 | psi | ISO 527-2 |
伸长率 |
|
|
|
|
断裂, 73°F | 3.2 | -- | % | ASTM D638 |
断裂, 73°F | 3.5 | 8.0 | % | ISO 527-2 |
弯曲模量 |
|
|
|
|
73°F | 1.20E+6 | -- | psi | ASTM D790 |
73°F | 1.25E+6 | 725000 | psi | ISO 178 |
弯曲应力 (73°F) | 39200 | 26100 | psi | ISO 178 |
简支梁缺口冲击强度 |
|
|
| ISO 179 |
-22°F | 5.2 | -- | ft·lb/in² |
|
73°F | 7.1 | 14 | ft·lb/in² |
|
简支梁无缺口冲击强度 |
|
|
| ISO 179 |
-22°F | 38 | -- | ft·lb/in² |
|
73°F | 45 | 52 | ft·lb/in² |
|
悬壁梁缺口冲击强度 |
|
|
|
|
-40°F | 1.8 | -- | ft·lb/in | ASTM D256 |
73°F | 2.0 | -- | ft·lb/in | ASTM D256 |
73°F | 7.1 | 9.5 | ft·lb/in² | ISO 180 |
载荷下热变形温度 |
|
|
|
|
66 psi, 未退火 | 428 | -- | °F | ASTM D648, ISO 75-2/B |
264 psi, 未退火 | 410 | -- | °F | ASTM D648, ISO 75-2/A |
熔融峰值温度 | 428 | -- | °F | ASTM D3418, ISO 3146 |
线形热膨胀系数 |
|
|
|
|
流动 | 1.1E-5 | -- | in/in/°F | ASTM E831 |
流动 | 1.3E-5 | -- | in/in/°F |
|
横向 | 3.6E-5 | -- | in/in/°F |
|
RTI Elec |
|
|
| UL 746 |
0.030 in | 248 | -- | °F |
|
0.06 in | 248 | -- | °F |
|
0.12 in | 248 | -- | °F |
|
RTI Imp |
|
|
| UL 746 |
0.06 in | 203 | -- | °F |
|
0.12 in | 203 | -- | °F |
|
RTI |
|
|
| UL 746 |
0.06 in | 266 | -- | °F |
|
0.12 in | 266 | -- | °F |
|
体积电阻率 |
|
|
|
|
0.0591 in | 1.0E+15 | 1.0E+12 | ohms·cm | ASTM D257 |
-- | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
介电常数 (1 MHz) | 3.80 | 6.80 |
| IEC 60250 |
耗散因数 |
|
|
| IEC 60250 |
100 Hz | 0.023 | 0.22 |
|
|
1 MHz | 0.023 | 0.22 |
|
|
UL 阻燃等级 |
|
|
| UL 94 |
0.06 in | HB | -- |
|
|
0.12 in | HB | -- |
|
|
如需巴斯夫原厂物性表及相关文件，请联系我们工作人员，谢谢！